Why Polyester Polymer concrete
- Reliability - known performance of 30+ years of Zero Maintenance
- Time to cure and ready for traffic - Ready to traffic in 2 Hours even in Cold and Humid Conditions
- Resistance to Chloride Permeability - Almost Zero
- Abrasion - 1 mm in 2.75 years compared to 4mm/year from using Portland Cement.
- Resistant to abrasion - maintains coefficient of friction - 0.4 over a proven period of 20 years
- Reduction of dead load (19 mm profile thickness)
- High Strength Properties
- 7- day Compressive yield – 41.4 MPa (422 kg/cm2)
- 7 - day Compressive Modulus – 10,342 MPa (105485 kg/cm2)
- 7 - day Flexural Strength -13.8 MPa (140 kg/cm2)
- Superior Adhesion with Concrete Base Substrate
- Highest performing bridge deck overlay and protection technology in the United States today.